{"id":3952,"date":"2024-06-27T15:17:39","date_gmt":"2024-06-27T15:17:39","guid":{"rendered":"https:\/\/machining-quote.com\/?p=3952"},"modified":"2024-07-01T01:17:43","modified_gmt":"2024-07-01T01:17:43","slug":"304-vs-2205-duplex-stainless-steel","status":"publish","type":"post","link":"https:\/\/machining-quote.com\/cs\/bolg\/304-vs-2205-duplex-stainless-steel\/","title":{"rendered":"Jak\u00fd je rozd\u00edl mezi nerezovou ocel\u00ed 304 a 2205 Duplex?"},"content":{"rendered":"<h4>Obsah<\/h4>\n<ul>\n<li><a href=\"#application-differences-when-to-use-304-vs-2205-duplex-stainless-steel\">Rozd\u00edly v aplikaci: Kdy pou\u017e\u00edt 304 vs. 2205 Duplex Stainless Steel<\/a><\/li>\n<li><a href=\"#heat-resistance-evaluating-304-and-2205-duplex-stainless-steel\">Tepeln\u00e1 odolnost: Hodnocen\u00ed 304 a 2205 Duplex Stainless Steel<\/a><\/li>\n<li><a href=\"#corrosion-resistance-comparing-304-and-2205-duplex-stainless-steel\">Odolnost proti korozi: Porovn\u00e1n\u00ed nerezov\u00e9 oceli 304 a 2205 Duplex<\/a><\/li>\n<li><a href=\"#composition-and-material-properties-304-vs-2205-duplex\">Slo\u017een\u00ed a vlastnosti materi\u00e1lu: 304 vs. 2205 Duplex<\/a><\/li>\n<li><a href=\"#mechanical-strength-and-durability-304-stainless-steel-vs-2205-duplex\">Mechanick\u00e1 pevnost a odolnost: Nerezov\u00e1 ocel 304 vs. 2205 Duplex<\/a><\/li>\n<li><a href=\"#welding-and-machining-techniques-for-304-and-2205-duplex-stainless-steel\">Sva\u0159ov\u00e1n\u00ed a obr\u00e1b\u011bn\u00ed: Techniky pro nerezovou ocel 304 a 2205 Duplex<\/a><\/li>\n<li><a href=\"#summary-chart-of-difference-between-304-and-2205-duplex-stainless-steel\">Souhrnn\u00e1 tabulka rozd\u00edl\u016f mezi nerezovou ocel\u00ed 304 a 2205 Duplex<\/a><\/li>\n<li><a href=\"#conclusion\">Z\u00e1v\u011br<\/a><\/li>\n<\/ul>\n<h2 id=\"application-differences-when-to-use-304-vs-2205-duplex-stainless-steel\">Rozd\u00edly v aplikaci: Kdy pou\u017e\u00edt 304 vs. 2205 Duplex Stainless Steel<\/h2>\n<h3>\u00davod<\/h3>\n<p>Nerezov\u00e1 ocel je z\u00e1kladn\u00edm stavebn\u00edm materi\u00e1lem ve stavebnictv\u00ed, stroj\u00edrenstv\u00ed a v\u00fdrob\u011b d\u00edky sv\u00e9 pevnosti, trvanlivosti a odolnosti proti korozi. Mezi r\u016fzn\u00fdmi t\u0159\u00eddami je zvl\u00e1\u0161t\u011b pozoruhodn\u00e1 duplexn\u00ed nerezov\u00e1 ocel 304 a 2205. Pochopen\u00ed jejich rozd\u00edl\u016f ve slo\u017een\u00ed, mechanick\u00fdch vlastnostech a odolnosti proti korozi je z\u00e1sadn\u00ed pro v\u00fdb\u011br vhodn\u00e9ho typu nerezov\u00e9 oceli pro konkr\u00e9tn\u00ed aplikace.<\/p>\n<h3>304 Nerezov\u00e1 ocel<\/h3>\n<p>Nerezov\u00e1 ocel 304, zn\u00e1m\u00e1 tak\u00e9 jako nerezov\u00e1 ocel 18\/8, je \u0161iroce pou\u017e\u00edv\u00e1na pro svou vynikaj\u00edc\u00ed tvarovatelnost a sva\u0159itelnost. Obsahuje p\u0159ibli\u017en\u011b 18% chrom a 8% nikl, je nemagnetick\u00fd a poskytuje dobrou odolnost v\u016f\u010di \u0161irok\u00e9 \u0161k\u00e1le chemik\u00e1li\u00ed a atmosf\u00e9rick\u00e9ho prost\u0159ed\u00ed. V chloridov\u00fdch prost\u0159ed\u00edch je v\u0161ak n\u00e1chyln\u00fd k d\u016flkov\u00e9 a \u0161t\u011brbinov\u00e9 korozi.<\/p>\n<h3>2205 Duplex Nerezov\u00e1 ocel<\/h3>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 m\u00e1 dvouf\u00e1zovou mikrostrukturu austenitu a feritu (p\u0159ibli\u017en\u011b 50\/50), kter\u00e1 poskytuje vynikaj\u00edc\u00ed pevnost a zv\u00fd\u0161enou odolnost proti prask\u00e1n\u00ed koroz\u00ed pod nap\u011bt\u00edm ve srovn\u00e1n\u00ed s nerezovou ocel\u00ed 304. S p\u0159ibli\u017en\u011b 22% chromem, 3% molybdenem a ni\u017e\u0161\u00edm obsahem niklu nab\u00edz\u00ed zv\u00fd\u0161enou odolnost proti d\u016flkov\u00e9 a \u0161t\u011brbinov\u00e9 korozi, zejm\u00e9na v prost\u0159ed\u00edch obsahuj\u00edc\u00edch chloridy.<\/p>\n<h3>Srovn\u00e1n\u00ed aplikac\u00ed<\/h3>\n<ul>\n<li><strong>Obecn\u00e9 aplikace:<\/strong> Nerezov\u00e1 ocel 304 je vhodn\u00e1 pro obecn\u00e9 aplikace, kde je vy\u017eadov\u00e1na tvarovatelnost, sva\u0159itelnost a odolnost proti korozi, jako jsou kuchy\u0148sk\u00e9 spot\u0159ebi\u010de a architektonick\u00e9 oblo\u017een\u00ed.<\/li>\n<li><strong>Drsn\u00e1 prost\u0159ed\u00ed:<\/strong> Duplexn\u00ed nerezov\u00e1 ocel 2205 se l\u00e9pe hod\u00ed pro vysoce nam\u00e1han\u00e9 aplikace a drsn\u00e1 prost\u0159ed\u00ed, jako jsou chemick\u00e9 zpracovatelsk\u00e9 z\u00e1vody a n\u00e1mo\u0159n\u00ed prost\u0159ed\u00ed, d\u00edky sv\u00e9 vynikaj\u00edc\u00ed pevnosti a odolnosti proti korozi.<\/li>\n<\/ul>\n<h3>\u00davahy o n\u00e1kladech<\/h3>\n<p>Zat\u00edmco nerezov\u00e1 ocel 304 je zpo\u010d\u00e1tku levn\u011bj\u0161\u00ed, jej\u00ed n\u00e1chylnost ke korozi v ur\u010dit\u00fdch prost\u0159ed\u00edch m\u016f\u017ee \u010dasem v\u00e9st k vy\u0161\u0161\u00edm n\u00e1klad\u016fm na \u00fadr\u017ebu a v\u00fdm\u011bnu. Vy\u0161\u0161\u00ed po\u010d\u00e1te\u010dn\u00ed n\u00e1klady na duplexn\u00ed nerezovou ocel 2205 mohou b\u00fdt kompenzov\u00e1ny del\u0161\u00ed \u017eivotnost\u00ed a ni\u017e\u0161\u00edmi n\u00e1roky na \u00fadr\u017ebu.<\/p>\n<h2 id=\"heat-resistance-evaluating-304-and-2205-duplex-stainless-steel\">Tepeln\u00e1 odolnost: Hodnocen\u00ed 304 a 2205 Duplex Stainless Steel<\/h2>\n<h3>304 Nerezov\u00e1 ocel<\/h3>\n<p>Nerezov\u00e1 ocel t\u0159\u00eddy 304, slo\u017een\u00e1 z chromu 18% a niklu 8%, vydr\u017e\u00ed vysok\u00e9 teploty a\u017e do p\u0159ibli\u017en\u011b 870 \u00b0C. Za t\u00edmto bodem jeho struktur\u00e1ln\u00ed integrita rychle degraduje. Nep\u0159etr\u017eit\u00e9 vystaven\u00ed teplot\u00e1m nad 500 \u00b0C m\u016f\u017ee v\u00e9st k v\u00fdrazn\u00e9mu usazov\u00e1n\u00ed vodn\u00edho kamene a sn\u00ed\u017een\u00ed mechanick\u00fdch vlastnost\u00ed.<\/p>\n<h3>2205 Duplex Nerezov\u00e1 ocel<\/h3>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 si zachov\u00e1v\u00e1 dobr\u00e9 mechanick\u00e9 vlastnosti a odolnost proti korozi p\u0159i teplot\u00e1ch do asi 300 \u00b0C a zvl\u00e1dne ob\u010dasn\u00e9 vystaven\u00ed a\u017e do teploty p\u0159ibli\u017en\u011b 600 \u00b0C. Duplexn\u00ed struktura poskytuje lep\u0161\u00ed odolnost proti tepeln\u00e9 rozta\u017enosti a prask\u00e1n\u00ed koroz\u00ed pod nap\u011bt\u00edm ve srovn\u00e1n\u00ed s 304.<\/p>\n<h3>Srovn\u00e1n\u00ed<\/h3>\n<table>\n<tbody>\n<tr>\n<th>Majetek<\/th>\n<th>304 Nerezov\u00e1 ocel<\/th>\n<th>2205 Duplex Nerezov\u00e1 ocel<\/th>\n<\/tr>\n<tr>\n<td>Maxim\u00e1ln\u00ed trval\u00e1 teplota<\/td>\n<td>870 \u00b0C<\/td>\n<td>300 \u00b0C<\/td>\n<\/tr>\n<tr>\n<td>P\u0159eru\u0161ovan\u00e1 teplota<\/td>\n<td>500 \u00b0C<\/td>\n<td>600 \u00b0C<\/td>\n<\/tr>\n<tr>\n<td>Tepeln\u00e1 rozta\u017enost<\/td>\n<td>Vy\u0161\u0161\u00ed<\/td>\n<td>Doln\u00ed<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<h2 id=\"corrosion-resistance-comparing-304-and-2205-duplex-stainless-steel\">Odolnost proti korozi: Porovn\u00e1n\u00ed nerezov\u00e9 oceli 304 a 2205 Duplex<\/h2>\n<h3>304 Nerezov\u00e1 ocel<\/h3>\n<p>Nerezov\u00e1 ocel t\u0159\u00eddy 304 nab\u00edz\u00ed vynikaj\u00edc\u00ed odolnost proti korozi v \u0161irok\u00e9m rozsahu atmosf\u00e9rick\u00fdch prost\u0159ed\u00ed a mnoha korozivn\u00edch m\u00e9di\u00ed. M\u016f\u017ee v\u0161ak bojovat v prost\u0159ed\u00ed s vystaven\u00edm chlorid\u016fm, jako jsou pob\u0159e\u017en\u00ed oblasti, co\u017e vede k d\u016flkov\u00e9 a \u0161t\u011brbinov\u00e9 korozi.<\/p>\n<h3>2205 Duplex Nerezov\u00e1 ocel<\/h3>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 s vy\u0161\u0161\u00edm obsahem chr\u00f3mu, molybdenu a niklu v\u00fdrazn\u011b zvy\u0161uje odolnost proti d\u016flkov\u00e9 a \u0161t\u011brbinov\u00e9 korozi v prost\u0159ed\u00edch obsahuj\u00edc\u00edch chloridy. Duplexn\u00ed struktura poskytuje vy\u0161\u0161\u00ed mez kluzu a lep\u0161\u00ed odolnost proti prask\u00e1n\u00ed koroz\u00ed pod nap\u011bt\u00edm.<\/p>\n<h3>Srovn\u00e1n\u00ed<\/h3>\n<ul>\n<li><strong>Obecn\u00e1 koroze:<\/strong> Ob\u011b t\u0159\u00eddy nab\u00edzej\u00ed dobrou odolnost, ale 2205 duplex funguje l\u00e9pe v prost\u0159ed\u00edch bohat\u00fdch na chloridy.<\/li>\n<li><strong>D\u016flkov\u00e1 a \u0161t\u011brbinov\u00e1 koroze:<\/strong> 2205 duplex nab\u00edz\u00ed vynikaj\u00edc\u00ed odolnost d\u00edky vy\u0161\u0161\u00edmu obsahu slitiny.<\/li>\n<\/ul>\n<h2 id=\"composition-and-material-properties-304-vs-2205-duplex\">Slo\u017een\u00ed a vlastnosti materi\u00e1lu: 304 vs. 2205 Duplex<\/h2>\n<h3>304 Nerezov\u00e1 ocel<\/h3>\n<p>Nerezov\u00e1 ocel 304, austenitick\u00e1 forma, se skl\u00e1d\u00e1 z chromu 18% a niklu 8%, co\u017e j\u00ed d\u00e1v\u00e1 vynikaj\u00edc\u00ed odolnost proti korozi a tvarovatelnost. Jeho plo\u0161n\u011b centrovan\u00e1 krychlov\u00e1 krystalick\u00e1 struktura poskytuje vysokou ta\u017enost a hou\u017eevnatost.<\/p>\n<h3>2205 Duplex Nerezov\u00e1 ocel<\/h3>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 m\u00e1 dvouf\u00e1zovou mikrostrukturu austenitu a feritu, kter\u00e1 poskytuje vyv\u00e1\u017een\u00e9 vlastnosti. Obvykle obsahuje chrom 22%, nikl 5% a molybden 3%, co\u017e zvy\u0161uje jeho pevnost a odolnost proti korozi.<\/p>\n<h3>Srovn\u00e1n\u00ed<\/h3>\n<table>\n<tbody>\n<tr>\n<th>Majetek<\/th>\n<th>304 Nerezov\u00e1 ocel<\/th>\n<th>2205 Duplex Nerezov\u00e1 ocel<\/th>\n<\/tr>\n<tr>\n<td>Obsah chromu<\/td>\n<td>18%<\/td>\n<td>22%<\/td>\n<\/tr>\n<tr>\n<td>Obsah niklu<\/td>\n<td>8%<\/td>\n<td>5%<\/td>\n<\/tr>\n<tr>\n<td>Obsah molybdenu<\/td>\n<td>0%<\/td>\n<td>3%<\/td>\n<\/tr>\n<tr>\n<td>Mikrostruktura<\/td>\n<td>austenitick\u00e9<\/td>\n<td>Austenit a ferit<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<h2 id=\"mechanical-strength-and-durability-304-stainless-steel-vs-2205-duplex\">Mechanick\u00e1 pevnost a odolnost: Nerezov\u00e1 ocel 304 vs. 2205 Duplex<\/h2>\n<h3>304 Nerezov\u00e1 ocel<\/h3>\n<p>Nerezov\u00e1 ocel 304 m\u00e1 mez kluzu asi 215 MPa (31 ksi), d\u00edky \u010demu\u017e je vhodn\u00e1 pro v\u0161eobecn\u00e9 pou\u017eit\u00ed, ale m\u00e9n\u011b ide\u00e1ln\u00ed pro aplikace vy\u017eaduj\u00edc\u00ed vysokou pevnost.<\/p>\n<h3>2205 Duplex Nerezov\u00e1 ocel<\/h3>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 m\u00e1 mez kluzu p\u0159ibli\u017en\u011b 450 MPa (65 ksi), poskytuje vynikaj\u00edc\u00ed mechanick\u00e9 vlastnosti a \u010din\u00ed z n\u00ed vynikaj\u00edc\u00ed volbu pro n\u00e1ro\u010dn\u00e9 aplikace.<\/p>\n<h3>Srovn\u00e1n\u00ed trvanlivosti<\/h3>\n<ul>\n<li><strong>Mez kluzu:<\/strong> Duplexn\u00ed nerezov\u00e1 ocel 2205 m\u00e1 dvojn\u00e1sobnou mez kluzu ne\u017e nerezov\u00e1 ocel 304.<\/li>\n<li><strong>S\u00edla \u00fanavy:<\/strong> 2205 duplex nab\u00edz\u00ed v\u011bt\u0161\u00ed \u00fanavovou pevnost.<\/li>\n<li><strong>\u017divotnost:<\/strong> 2205 duplex poskytuje del\u0161\u00ed \u017eivotnost a ni\u017e\u0161\u00ed n\u00e1klady na \u00fadr\u017ebu.<\/li>\n<\/ul>\n<h2 id=\"welding-and-machining-techniques-for-304-and-2205-duplex-stainless-steel\">Sva\u0159ov\u00e1n\u00ed a obr\u00e1b\u011bn\u00ed: Techniky pro nerezovou ocel 304 a 2205 Duplex<\/h2>\n<h3>Sva\u0159ovac\u00ed techniky<\/h3>\n<p>Sva\u0159ov\u00e1n\u00ed nerezov\u00e9 oceli 304 je d\u00edky sv\u00e9 austenitick\u00e9 struktu\u0159e pom\u011brn\u011b jednoduch\u00e9. Mezi b\u011b\u017en\u00e9 postupy pat\u0159\u00ed pou\u017eit\u00ed austenitick\u00fdch p\u0159\u00eddavn\u00fdch kov\u016f a zaji\u0161t\u011bn\u00ed spr\u00e1vn\u00e9ho p\u0159\u00edvodu tepla a interpass teplot.<\/p>\n<p>Sva\u0159ov\u00e1n\u00ed duplexn\u00ed nerezov\u00e9 oceli 2205 vy\u017eaduje v\u011bt\u0161\u00ed p\u0159esnost, aby byla zachov\u00e1na jej\u00ed duplexn\u00ed mikrostruktura. Je velmi d\u016fle\u017eit\u00e9 pou\u017e\u00edvat p\u0159\u00eddavn\u00e9 kovy duplexn\u00ed kvality a \u0159\u00eddit p\u0159\u00edvod tepla, aby se zabr\u00e1nilo tvorb\u011b \u0161kodliv\u00fdch f\u00e1z\u00ed.<\/p>\n<h3>Techniky obr\u00e1b\u011bn\u00ed<\/h3>\n<ul>\n<li><strong>304 Nerezov\u00e1 ocel:<\/strong> Sn\u00e1ze se obr\u00e1b\u00ed ne\u017e duplexn\u00ed t\u0159\u00eddy, ale m\u00e1 tendenci ztvrdnout. Ostr\u00e9 n\u00e1stroje a spr\u00e1vn\u00e9 parametry obr\u00e1b\u011bn\u00ed jsou z\u00e1sadn\u00ed.<\/li>\n<li><strong>2205 Duplex Nerezov\u00e1 ocel:<\/strong> Vy\u017eaduje vysokorychlostn\u00ed n\u00e1stroje a dostate\u010dn\u00e9 maz\u00e1n\u00ed, aby se sn\u00ed\u017eilo vytv\u00e1\u0159en\u00ed tepla a zabr\u00e1nilo se p\u0159ed\u010dasn\u00e9mu opot\u0159eben\u00ed n\u00e1stroje.<\/li>\n<\/ul>\n<h2 id=\"summary-chart-of-difference-between-304-and-2205-duplex-stainless-steel\">Souhrnn\u00e1 tabulka rozd\u00edl\u016f mezi nerezovou ocel\u00ed 304 a 2205 Duplex<\/h2>\n<table>\n<tbody>\n<tr>\n<th>Majetek<\/th>\n<th>304 Nerezov\u00e1 ocel<\/th>\n<th>2205 Duplex Nerezov\u00e1 ocel<\/th>\n<\/tr>\n<tr>\n<td>Obsah chromu<\/td>\n<td>18%<\/td>\n<td>22%<\/td>\n<\/tr>\n<tr>\n<td>Obsah niklu<\/td>\n<td>8%<\/td>\n<td>5%<\/td>\n<\/tr>\n<tr>\n<td>Obsah molybdenu<\/td>\n<td>0%<\/td>\n<td>3%<\/td>\n<\/tr>\n<tr>\n<td>Mikrostruktura<\/td>\n<td>austenitick\u00e9<\/td>\n<td>Austenit a ferit<\/td>\n<\/tr>\n<tr>\n<td>Pevnost v tahu<\/td>\n<td>215 MPa<\/td>\n<td>450 MPa<\/td>\n<\/tr>\n<tr>\n<td>Odolnost proti korozi<\/td>\n<td>Dobr\u00fd<\/td>\n<td>Vynikaj\u00edc\u00ed<\/td>\n<\/tr>\n<tr>\n<td>Tepeln\u00e1 odolnost<\/td>\n<td>A\u017e 870\u00b0C<\/td>\n<td>A\u017e 300\u00b0C<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n<h2 id=\"conclusion\">Z\u00e1v\u011br<\/h2>\n<p>Hlavn\u00ed rozd\u00edl mezi nerezovou ocel\u00ed 304 a duplexn\u00ed nerezovou ocel\u00ed 2205 spo\u010d\u00edv\u00e1 v jejich chemick\u00e9m slo\u017een\u00ed a mechanick\u00fdch vlastnostech. Nerezov\u00e1 ocel 304, austenitick\u00e9ho typu, se skl\u00e1d\u00e1 z 18% chr\u00f3mu a 8% niklu, d\u00edky \u010demu\u017e je vysoce odoln\u00e1 v\u016f\u010di korozi a oxidaci. Je \u0161iroce pou\u017e\u00edv\u00e1n pro svou snadnou v\u00fdrobu a p\u016fsobivou odolnost proti korozi v m\u00edrn\u00fdch prost\u0159ed\u00edch.<\/p>\n<p>Duplexn\u00ed nerezov\u00e1 ocel 2205 kombinuje vlastnosti austenitick\u00fdch i feritick\u00fdch nerezov\u00fdch ocel\u00ed, typicky obsahuj\u00edc\u00edch p\u0159ibli\u017en\u011b 22% chrom, 5% nikl a 3% molybden. Toto slo\u017een\u00ed poskytuje vynikaj\u00edc\u00ed pevnost a zv\u00fd\u0161enou odolnost proti korozi, zejm\u00e9na korozn\u00edmu prask\u00e1n\u00ed pod nap\u011bt\u00edm. Je vhodn\u011bj\u0161\u00ed pro drsn\u00e1 prost\u0159ed\u00ed, nab\u00edz\u00ed vy\u0161\u0161\u00ed pevnost v tahu a mez kluzu.<\/p>\n<p>Z\u00e1v\u011brem lze \u0159\u00edci, \u017ee zat\u00edmco nerezov\u00e1 ocel 304 je v\u00fdhodn\u011bj\u0161\u00ed pro obecnou odolnost proti korozi a snadnou v\u00fdrobu, duplexn\u00ed nerezov\u00e1 ocel 2205 nab\u00edz\u00ed v\u011bt\u0161\u00ed pevnost a trvanlivost, tak\u017ee je vhodn\u00e1 pro n\u00e1ro\u010dn\u00e9 aplikace, kde je vy\u017eadov\u00e1na vy\u0161\u0161\u00ed odolnost v\u016f\u010di korozi a nam\u00e1h\u00e1n\u00ed. P\u0159i v\u00fdb\u011bru mezi t\u011bmito dv\u011bma materi\u00e1ly zva\u017ete podm\u00ednky prost\u0159ed\u00ed, mechanick\u00e9 po\u017eadavky a ekonomick\u00e9 faktory souvisej\u00edc\u00ed s va\u0161\u00ed aplikac\u00ed, abyste zajistili optim\u00e1ln\u00ed v\u00fdkon a n\u00e1kladovou efektivitu.<\/p>","protected":false},"excerpt":{"rendered":"<p>Table of Contents Application Differences: When to Use 304 vs. 2205 Duplex Stainless Steel Heat Resistance: Evaluating 304 and 2205 Duplex Stainless Steel Corrosion Resistance: Comparing 304 and 2205 Duplex Stainless Steel Composition and Material Properties: 304 vs. 2205 Duplex Mechanical Strength and Durability: 304 Stainless Steel vs. 2205 Duplex Welding and Machining: Techniques for [&hellip;]<\/p>","protected":false},"author":1,"featured_media":4021,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"_gspb_post_css":"","content-type":"","footnotes":""},"categories":[3],"tags":[],"class_list":["post-3952","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-material-selection-guide"],"blocksy_meta":[],"_links":{"self":[{"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/posts\/3952","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/comments?post=3952"}],"version-history":[{"count":2,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/posts\/3952\/revisions"}],"predecessor-version":[{"id":3955,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/posts\/3952\/revisions\/3955"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/media\/4021"}],"wp:attachment":[{"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/media?parent=3952"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/categories?post=3952"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/machining-quote.com\/cs\/wp-json\/wp\/v2\/tags?post=3952"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}