304L and 430 stainless steels have unique properties and uses. 304L has high corrosion resistance and is good for welding. 430 is ferritic, with good formability and moderate corrosion resistance. Knowing their differences helps you choose the right material for your needs.
What Are the Equivalents of 304L and 430 Stainless Steel?
Equivalents of 304L Stainless Steel
- European Standard: 1.4307, 1.4301
- Japanese Standard: SUS304L
Equivalents of 430 Stainless Steel
- European Standard: 1.4016
- Japanese Standard: JIS G4305
Keskeiset erot
| Kiinteistö | 304 litraa | 430 |
|---|
| Nikkelipitoisuus | Korkeampi | Very Low |
| Korroosionkestävyys | Korkea | Kohtalainen |
| Hitsattavuus | Erinomainen | Rajoitettu |
| Muovattavuus | Hyvä | Hyvä |
| Kustannukset | Korkeampi | Alempi |
Corrosion Resistance Comparison: 304L and 430
304L ruostumaton teräs
- Higher chromium (18-20%) and nickel (8-12%) content.
- Excellent in acidic and chlorinated environments.
- Ideal for chemical processing, outdoor equipment, and kitchen appliances.
430 ruostumatonta terästä
- Lower chromium (16-18%) and almost no nickel.
- Good in mild environments.
- Used in appliances, automotive trim, and indoor architecture.
Vertailukaavio
| Kiinteistö | 304 litraa | 430 |
|---|
| Kromipitoisuus | 18-20% | 16-18% |
| Nikkelipitoisuus | 8-12% | <0.75% |
| Kestävyys klorideille | Korkea | Matala |
| Soveltuvuus meriympäristöön | Korkea | Matala |
Surface Finish and Aesthetic Differences: 304L vs 430
304L ruostumaton teräs
- High polish potential.
- Smooth finish after processing.
- Ideal for visible and sanitary applications.
430 ruostumatonta terästä
- High reflectivity but highlights imperfections.
- Good for decorative applications.
- Less smooth finish compared to 304L.
Vertailutaulukko
| Kiinteistö | 304 litraa | 430 |
|---|
| Finish Quality | Korkea | Kohtalainen |
| Polish Potential | Korkea | Korkea |
| Application Areas | Sanitary, visible areas | Decorative, less demanding areas |
Composition and Properties: 304L vs 430 Stainless Steel
304L ruostumaton teräs
- Austenitic structure.
- 18-20% chromium, 8-12% nickel.
- Excellent corrosion resistance.
- Good at high temperatures.
430 ruostumatonta terästä
- Ferritic structure.
- 16-18% chromium, almost no nickel.
- Moderate corrosion resistance.
- Magnetic properties.
Properties Comparison
| Kiinteistö | 304 litraa | 430 |
|---|
| Kromipitoisuus | 18-20% | 16-18% |
| Nikkelipitoisuus | 8-12% | <0.75% |
| Korroosionkestävyys | Korkea | Kohtalainen |
| Magneettinen | Ei | Kyllä |
| Kustannukset | Korkeampi | Alempi |
Heat Treatment Processes for 304L and 430 Stainless Steels
304L ruostumaton teräs
- Annealing at 1900°F (1040°C).
- Relieves internal stresses.
- Makes the metal more ductile.
430 ruostumatonta terästä
- Temper rolling or skin passing.
- Improves surface finish and hardness.
- Sub-critical anneal at 1400-1500°F.
Vertailu
| Kiinteistö | 304 litraa | 430 |
|---|
| Heat Treatment Method | Hehkutus | Temper rolling, Sub-critical anneal |
| Lämpötila-alue | 1900°F | 1400-1500°F |
| Effect on Material | Relieves stress, increases ductility | Improves finish and hardness |
Mechanical Strength: 304L vs 430 Stainless Steel
304L ruostumaton teräs
- Tensile strength: 485 MPa
- Yield strength: 170 MPa
- Elongation: 40%
430 ruostumatonta terästä
- Tensile strength: 450 MPa
- Syötön lujuus: 310 MPa
- Elongation: 25%
Vahvuuden vertailu
| Kiinteistö | 304 litraa | 430 |
|---|
| Vetolujuus | 485 MPa | 450 MPa |
| Myötölujuus | 170 MPa | 310 MPa |
| Venymä | 40% | 25% |
| Rakenne | Austeniittista | Ferritic |
Machining Capabilities of 304L and 430 Stainless Steels
304L ruostumaton teräs
- Excellent corrosion resistance.
- Weldability is high.
- Harder to machine due to work hardening.
430 ruostumatonta terästä
- Good corrosion resistance.
- More affordable.
- Easier to machine with higher cutting speeds.
Machining Comparison
| Kiinteistö | 304 litraa | 430 |
|---|
| Työstettävyys | Haastava | Helppo |
| Työn kovettuminen | Korkea | Matala |
| Leikkausnopeus | Slower | Faster |
| Työkalujen kuluminen | Korkeampi | Alempi |
Applications: Choosing Between 304L and 430 Stainless Steel
304L ruostumaton teräs
- Elintarvikkeiden jalostuslaitteet
- Lääketieteelliset laitteet
- Architectural paneling
430 ruostumatonta terästä
- Autojen verhoilu
- Kitchen utensils
- Kodinkoneet
Soveltuvuus
| Hakemus | 304 litraa | 430 |
|---|
| Food Industry | Erinomainen | Hyvä |
| Autoteollisuus | Hyvä | Erinomainen |
| Cost-sensitive Projects | Kohtalainen | Erinomainen |
| Welded Structures | Erinomainen | Kohtalainen |
304L Stainless vs 430: Which is Better?
Huomioon otettavat tekijät
- Korroosionkestävyys
- Mechanical strength
- Kustannukset
- Specific application requirements
304L ruostumaton teräs
- High corrosion resistance
- Good for welding
- Korkeammat kustannukset
430 ruostumatonta terästä
- Kohtalainen korroosionkestävyys
- Magneettiset ominaisuudet
- Alempi kustannus
Decision Chart
| Kriteeri | 304 litraa | 430 |
|---|
| Korroosionkestävyys | Korkea | Kohtalainen |
| Kustannukset | Korkeampi | Alempi |
| Hitsattavuus | Erinomainen | Rajoitettu |
| Sovellukset | Wide range, harsh environments | Cost-effective, mild environments |
Summary Chart of What is the Difference Between 304L and 430 Stainless Steel
| Kiinteistö | 304 litraa | 430 |
|---|
| Kromipitoisuus | 18-20% | 16-18% |
| Nikkelipitoisuus | 8-12% | <0.75% |
| Korroosionkestävyys | Korkea | Kohtalainen |
| Hitsattavuus | Erinomainen | Kohtalainen |
| Magneettinen | Ei | Kyllä |
| Kustannukset | Korkeampi | Alempi |
| Tyypilliset sovellukset | Food processing, medical devices, architecture | Automotive, kitchen utensils, appliances |
Päätelmä
304L and 430 stainless steels differ in composition, corrosion resistance, and cost. 304L is highly resistant to corrosion, good for welding, and more expensive. 430 is moderately resistant to corrosion, magnetic, and more affordable. Choose based on your application’s specific needs, balancing performance and cost.